Titanium and the SR-71

Today we are going to look at Titanium and the SR-71. For anyone not familiar with this amazing feat of engineering please read this article

Innovation owes much to the materials used to create it. Last month we looked at the material design which gives the Tesla Cybertruck its unique look. You can read that article here.

The SR-71, or to give its full name, the Lockheed SR-71 Blackbird was created during the 1060s. It was a project envisioned and operated by the United States Air Force and NASA.

Just some Records held by the SR-71

  • Altitude in Horizontal Flight: 85,068.997 feet
  • Speed Over a Straight Course – Average Speed: 2,193.167 mph
  • Speed Over a Recognized Course: New York to London: 1 hour, 54 minutes, 56.4 seconds

The SR-71’s speed was not limited by the power of its engines. It was limited by the heat it’s structure could withstand. Today we are going to explore the relationship between Titanium and the SR-71. Titanium makes up 93% of the SR-71s structure. A material that had never been truly utilized to its full potential until the SR-71 came along.

What is Titanium?

Titanium is one of those words that has entered the common language. It’s become synonymous with strength. The singer Sia likens titanium to being bulletproof, and yes with the right thickness it is bulletproof.

But, in reality, the strongest titanium alloys are only about as strong as the strongest steel alloys. In fact, their temperature tolerance is actually worse, while Aluminium is lighter. What makes titanium special is not it’s tensile strength, weight, or high-temperature performance. It is a combination of all of these material properties that made it perfect for the SR-71.

To say that Titanium is a Jack of all trades, master of none is a disservice to it. Titanium and the SR-71 work together because of these mixed properties.

Material Selection

When choosing materials for a particular application, engineers will often consult something called a material selection diagram. Where we plot two material properties on the x and y axes. This allows us to see the relative benefits of materials so we can choose a material according to our needs.

Strength vs Relative Cost Per Volume diagram

Steel is by far the heaviest, which rules it out of most aircraft structures. Actually it still gets used where its strength and heat tolerance are needed. We can also see that Aluminium is in fact lighter than Titanium, but Titanium is stronger than Aluminium. A better measure here is the strength to weight ratio. A ratio found by dividing the strength of the metal by its density.

After all, we can make an aluminum part stronger by just adding more material. But, if we need to add so much material that the part is now heavier than an equivalent strength part made from Titanium.

Here Titanium wins. It’s strength to weight ratio, or specific strength, is better than Aluminium. Yet today very little titanium is used in everyday objects. Planes primarily use aluminum, not titanium.

Why is Titanium used on the SR 71 not used on planes?

Why is that? One reason: It’s really expensive. Despite titanium being the 9th most common element in earth’s crust at a percent weight of 0.6%. There is more titanium in the earth’s crust than carbon, an element no-one considers rare.

Yet, in it’s purified form it currently costs about four and a half thousand dollars per metric tonne. Aluminum in comparison costs a third of that at a grand and a half per metric tonne. It is a relatively expensive metal as a result of its high energy electrolysis refinement process. To boot, that is today’s price which has dropped dramatically since the SR-71 was created.

Titanium is expensive because it’s refinement process is a nightmare. To make Titanium, we start with a feedstock in the form of Titanium Dioxide, with this chemical formula. This oxide ore called rutile can be found in high concentrations in these dark sandy soils.

Titanium, the SR 71, and the Soviets

To build the SR-71 the US needed to buy vast quantities of the mineral from the Soviets. To do this they purchased the material through ghost organizations to hide the final destination of the material.

Had the Soviets known what they were helping build, they would not have sold material. However, the US likely could have just purchased the material from mines in Australia. This is a relatively common raw material and is primarily used as a white pigment for paints and is even found in sunscreen lotion as ultraviolet radiation blocking pigment.

How we get Titanium

Our trouble begins when we need to separate those two oxygen molecules to get pure titanium. Iron is heated in the presence of carbon to force the oxygen to separate. This binds with carbon to form carbon dioxide.

Aluminum oxide’s melting point is too high, so we instead dissolve it in a solvent. And then use electrolysis to separate the oxygen molecule. Neither of these methods works with Titanium. Titanium dioxide is both thermally stable and resistant to chemical attack.

The first reliable process to produce chemically pure titanium was developed in the 1940s. This process made the SR-71 possible. It begins by first converting the titanium dioxide to titanium chloride.

How do we convert the Titanium?

To do this titanium dioxide is mixed with chlorine and pure carbon and heated. Any oxygen or nitrogen leaking in will ruin the process, so this has to be done in relatively small batches in a sealed vessel. Once this process is complete, we have Titanium Chloride.

We then need to purify the Titanium Chloride from any impurities in the titanium ore through distillation. Where we heat the product and separate titanium chloride using it’s lower boiling point.

This Titanium Chloride vapor is fed into a stainless steel vessel containing molten magnesium at 1300 kelvin. Titanium is highly reactive with oxygen at high temperatures, so the vessel also needs to be sealed and filled with argon. Here the Titanium Chloride reacts with the magnesium, which itself is an expensive metal, to form titanium and magnesium chloride.

Converting Titanium for the SR-71 is really slow

This reduction reaction is extremely slow, between 2 and 4 days. Once the reaction is complete we need to let the product cool. Before removing the magnesium chloride products through high-temperature distillation once again. The magnesium and chlorine are recycled with electrolysis, another energy-intensive process.

At this stage, we have titanium sponge, which needs further processing still. Typically a porous metal like this would be simply heated and compressed into rolls of sheet metal. O some other form of the useful end product. But Titanium will react with oxygen and nitrogen if heated this high, we can’t do that.

So the titanium sponge is compressed into an electrode along with any alloying alloys needed. Heat is then generated through an electric arc current inside another sealed vessel. This form of heat needs no oxygen. This melts the electrode to form a large titanium ingot.

This process results in an incredibly expensive material.

The SR-71 Engineers’ Solutions

The engineers of the SR-71 were among the first people in history to make real use of the material. In that process, they ended up throwing away a lot of material, some through necessity, some through error. At times the engineers were perplexed as to what was causing problems, but thankfully they documented and cataloged everything, which helped find trends in their failures.

They discovered that spot welded parts made in the summer were failing very early in their life, but those welded in winter were fine. They eventually tracked the problem to the fact that the Burbank water treatment facility was adding chlorine to the water they used to clean the parts to prevent algae blooms in summer, but took it out in winter. Chlorine as we saw earlier reacts with titanium, so they began using distilled water from this point on.

They discovered that their cadmium plated tools were leaving trace amounts of cadmium on bolts, which would cause galvanic corrosion and cause the bolts to fail. This discovery led to all cadmium tools to be removed from the workshop.

Manufacturing had to catch up

However, the largest wastes were caused by the lack of appropriate forging presses in the United States. Titanium alloys require much higher pressure to deform during forging than aluminum alloys or steel alloys.

The best forge in the US could only produce 20% of the pressure needed to form these titanium parts. Clarence L Johnson, the manager of Skunk Works at the time pleaded for the development of an adequate forging press. He stated it would need to be a 250,000-ton metal forming press.

Because of these inadequacies in forming capabilities, the final forging dimensions were nowhere near the design dimensions and much of the forming process had to be completed through machining. Meaning, most of the material was cut away to form the part, resulting in 90% of the material going to waste. When your raw material costs this much, this kind of waste really hurts.

Titanium is difficult

To add insult to injury. Drill bits and other machining tools were being thrown away at a rapid pace. Titanium is a difficult material to machine, precisely because of its qualities that made it suitable for use in the SR-71.

The skin panels were fastened to the underlying structure with oblong holes which would allow the skin to expand and contract without the fasteners causing buckling. And the skin over the wing was also corrugated to prevent warping during expansion, this is actually quite noticeable, you can see the sections that are corrugated quite clearly here.

This didn’t affect machining difficulties, but the extremely low thermal conductivity did. Machining materials produce a lot of heat that can damage the tool and cause unfavorable material properties in the titanium, like hardening. This means the metal under the fresh cut is now harder, and therefore even more damaging to the tool. This is usually minimized with coolant, but titanium’s low thermal conductivity means very little heat is transferred into the coolant.

Slowing it down

To deal with this lower machining speeds need to be used along with high volumes of coolant, which is also expensive. This slows the rate heat is generated and increases the rate it is removed.

This slower machine speed makes the process incredibly slow, but this is offset by taking larger cuts in each pass, which has the added benefit of cutting under the work-hardened layers.

Titanium is also more sensitive to dull tools, as it’s stiffness is quite low. Machinists refer to metals like this as being gummy. They tend to form long chips that can clog the work area and cause all sorts of problems. If not properly managed they can ruin the work surface and damage the tools.
The engineers at Lockheed gradually learned these lessons and developed better tools for the job.

When the first version of the SR-71 was being constructed, the drill bits used to cut the holes for the rivets could only drill 17 holes before they were unusable and needed to be discarded. By the end of the SR-71 program, they had developed a new drill bit that could drill 100 holes and then be sharpened for further use.

How to Save $19 million

By the end of the program, the engineers had found enough improvements to save 19 million dollars on the manufacturing. It’s pretty clear that titanium is expensive and extremely difficult to work with. But without Titanium and the SR-71, we wouldn’t be where we are today. Aluminum was an option. But Aluminium simply cannot deal with the temperatures that steel and titanium can.

Titanium hates Oxygen

Titanium alloys maintain a great deal of their strength up to temperatures as high as 842 Fahrenheit. The same cannot be said for aluminum.

Pure titanium is highly reactive to oxygen, which forms an oxide layer on the outside of the metal which is brittle. This oxide layer has some benefits as it provides excellent corrosion resistance which is why many submarines use titanium to resist attack from salt water.

But at higher temperatures this oxide layer and titanium are soluble to oxygen, which means the oxygen can permeate through the outer oxide layer and diffuse into the metal, causing the oxide layer to grow and eventually helps dangerous cracks to form.

The primary titanium alloy used in the SR-71 was thirteen percent vanadium, eleven percent chromium, and three percent aluminum. Both Chromium and Aluminium form thermally stable oxide layers on the outer skin of the metal. Which prevents oxygen from diffusing further into the metal and causing it to become more brittle. Which raises the max operating temperature of the metal.

Vanadium acts as a stabilizer for a crystal structure referred to as the beta phase. This leads to a material with higher tensile strength and better formability.

Titanium and the SR-71 Conclusion

Titanium and the SR-71 conclusion. Such advancements in material science like this have the largest knock-on effect on the advancement of human technologies. So much so, that we name entire eras of human history after the materials we developed during that time; Bronze Age, Iron Age, etc.

This Post Has 2 Comments

  1. Michelle

    Thank you for this article. Interesting to say the least.
    I am curious about ancient methods of metal and alloy manufacture although it is well out of my comfort zone. Any chance of such an article on ancient Copper, Tin, Zinc, Brass & Bronze etc. showing the ores commonly used, the then methods of extraction/purification and the properties of the results. Even how the Romans made their weapons from iron would be of value. I really hope that my interest is only theoretical but you never know NPs if not of interest.